We are providing wide range of whole tyre reclaim rubber and these are quality tested at our quality testing unit. With high quality standard and strict quality control system, these range meet the international standard. Extensive Refined Reclaim Rubber obtained by reclamation from scrap tyre. High tensile,High Mooney / Low Mooney reclaimed rubber and Special grade reclaimed rubber as per customer specification can be provided.
MATERIAL CHARACTERIZATION
APPEARANCE : BLACK SLAB 0.5 to 0.75 Inch thick
COLOUR : BLACK
TENSILE STRENGTH : GOOD TENSILE AND AGEING PROPERTIES, FREE FROM FIBROUS / METALIC MATERIALS, BLENDED WHOLE TYRE RECLAIM. HIGH TENSILE, MAXIMUM REFINING TO GIVE SMOOTH APPEARANCE
PACKING : 50 KG HDPE BAGS, LABLE IN BLUE INK OR Tied with Carristrap in bare packing
MARKING : NAME OF MATERIAL/ OUR DETAILS/ DATE OF MFG/ GRADE CODE / QTY
MK-01-HT SUPERFINE GRADE – HIGH TENSILE
Item Description: Reclaimed Rubber – WTR-HT Grade: MK – 01 HT (Superfine)
| No | Particulars | TARGET | MIN | MAX | METHOD |
|---|---|---|---|---|---|
| 1 | Ash Content (%) | 7.0 | 4.0 | 09.0 | IS 6306-1971 |
| 2 | Acetone Extract (%) | 14.0 | 9.0 | 18.0 | IS 6306-1971 |
| 3 | Carbon Black (%) | 26.0 | 22.0 | 30.0 | IS 6306-1971 |
| 4 | Rubber Hydro Carbon (%) | ---- | 45.0 | ----- | IS 6306-1971 |
| 5 | Specific gravity (gm/cm³) | 1.15 | 1.10 | 1.20 | IS 6306-1971 |
| 6 | Mooney Viscosity ML(1+4)@100ºC | 30.0 | 20.0 | 45.0 | IS 6306-1971 |
| 7 | Tensile Strength (PSI) | 900.0 | 800.0 | ---- | IS 3400-1987 |
| 8 | Elongation at Break(%) | --- | 180.0 | ---- | IS 3400-1987 |
| 9 | T5 | 5.50 | 4.50 | ---- | ASTM D 1646 |
| 10 | Volatile matter (%) | --- | --- | 1.10 | IS 6306-1971 |
MK – 01 SUPERFINE GRADE
Item Description: Reclaimed Rubber – WTR Grade: MK – 01 (Superfine)
| No | Particulars | TARGET | MIN | MAX | METHOD |
|---|---|---|---|---|---|
| 1 | Ash Content (%) | 7.0 | 4.0 | 09.0 | IS 6306-1971 |
| 2 | Acetone Extract (%) | 14.0 | 9.0 | 18.0 | IS 6306-1971 |
| 3 | Carbon Black (%) | 26.0 | 22.0 | 30.0 | IS 6306-1971 |
| 4 | Rubber Hydro Carbon (%) | ---- | 45.0 | ----- | IS 6306-1971 |
| 5 | Specific gravity (gm/cm³) | 1.15 | 1.10 | 1.20 | IS 6306-1971 |
| 6 | Mooney Viscosity ML(1+4)@100ºC | 30.0 | 20.0 | 45.0 | IS 6306-1971 |
| 7 | Tensile Strength (kg/cm²) | 45.0 | 40.0 | ---- | IS 3400-1987 |
| 8 | Elongation at Break(%) | --- | 180.0 | ---- | IS 3400-1987 |
| 9 | T5 | 5.50 | 4.50 | ---- | ASTM D 1646 |
| 10 | Volatile matter (%) | --- | --- | 1.10 | IS 6306-1971 |
MK – 02 FINE GRADE
Item Description: Reclaimed Rubber – WTR Grade:MK – 02 (Fine)
| No | Particulars | TARGET | MIN | MAX | METHOD |
|---|---|---|---|---|---|
| 1 | Ash Content (%) | 7.0 | 4.0 | 09.0 | IS 6306-1971 |
| 2 | Acetone Extract (%) | 14.0 | 9.0 | 18.0 | IS 6306-1971 |
| 3 | Carbon Black (%) | 26.0 | 22.0 | 30.0 | IS 6306-1971 |
| 4 | Rubber Hydro Carbon (%) | ---- | 45.0 | ----- | IS 6306-1971 |
| 5 | Specific gravity (gm/cm³) | 1.15 | 1.10 | 1.20 | IS 6306-1971 |
| 6 | Mooney Viscosity ML(1+4)@100ºC | 30.0 | 20.0 | 45.0 | IS 6306-1971 |
| 7 | Tensile Strength (kg/cm²) | 45.0 | 40.0 | ---- | IS 3400-1987 |
| 8 | Elongation at Break(%) | --- | 180.0 | ---- | IS 3400-1987 |
| 9 | T5 | 5.50 | 4.50 | ---- | ASTM D 1646 |
| 10 | Volatile matter (%) | --- | --- | 1.10 | IS 6306-1971 |
MK – 03 MEDIUM GRADE
Item Description: Reclaimed Rubber – WTR Grade:MK – 03 (Medium)
| No | Particulars | TARGET | MIN | MAX | METHOD |
|---|---|---|---|---|---|
| 1 | Ash Content (%) | 7.0 | 6.0 | 10.0 | IS 6306-1971 |
| 2 | Acetone Extract (%) | 14.0 | 9.0 | 18.0 | IS 6306-1971 |
| 3 | Carbon Black (%) | 26.0 | 22.0 | 30.0 | IS 6306-1971 |
| 4 | Rubber Hydro Carbon (%) | ---- | 40.0 | ----- | IS 6306-1971 |
| 5 | Specific gravity (gm/cm³) | 1.15 | 1.10 | 1.20 | IS 6306-1971 |
| 6 | Mooney Viscosity ML(1+4)@100ºC | ---- | 30.0 | 55.0 | IS 6306-1971 |
| 7 | Tensile Strength (kg/cm²) | ---- | 35.0 | ---- | IS 3400-1987 |
| 8 | Elongation at Break(%) | --- | 130.0 | ---- | IS 3400-1987 |
| 9 | T5 | ---- | ---- | ---- | ASTM D 1646 |
| 10 | Volatile matter (%) | ---- | --- | 1.10 | IS 6306-1971 |
MK – 04 COARSE GRADE
Item Description: Reclaimed Rubber – WTR Grade:MK – 04 (Coarse)
| No | Particulars | TARGET | MIN | MAX | METHOD |
|---|---|---|---|---|---|
| 1 | Ash Content (%) | 7.0 | 6.0 | 10.0 | IS 6306-1971 |
| 2 | Acetone Extract (%) | 14.0 | 9.0 | 18.0 | IS 6306-1971 |
| 3 | Carbon Black (%) | 26.0 | 22.0 | 30.0 | IS 6306-1971 |
| 4 | Rubber Hydro Carbon (%) | ---- | 40.0 | ----- | IS 6306-1971 |
| 5 | Specific gravity (gm/cm³) | ---- | ---- | ---- | IS 6306-1971 |
| 6 | Mooney Viscosity ML(1+4)@100ºC | ---- | 30.0 | 55.0 | IS 6306-1971 |
| 7 | Tensile Strength (kg/cm²) | ---- | 35.0 | ---- | IS 3400-1987 |
| 8 | Elongation at Break(%) | --- | 130.0 | ---- | IS 3400-1987 |
| 9 | T5 | ---- | ---- | ---- | ASTM D 1646 |
| 10 | Volatile matter (%) | ---- | ---- | 1.10 | IS 6306-1971 |
APPLICATION
Reclaim rubber widely used in Truck Tyres, Tread Rubber and Rubber Moulded Components. Moderately refined reclaim rubber mainly used in Cycle Tyres, Rubber Mat, Battery Containers and also in molded rubber products. Coarse reclaim rubber mainly used in Tyre Flaps, Mats, Pedal Rubber, Rubber Sheets Floor/ Coir Matt etc…
ADVANTAGES
• Shorter and faster mixing cycles.
• Improved die swell, adhesion, permeability.
• Reduction in consumption of electrical power due to nerve of compound and faster mixing cycle.
• Practically no reduction in hot air ageing properties.
• Fewer compounds at less cost.
• Low calendaring and extrusion temperature.
MKR-01 REACH Compliant Reclaimed Rubber
MKR-01 is our special grade for Reach compliant reclaimed rubber. We can supply all grades and many types of reclaimed rubber suitable for European market, based on your requirements.